MgO-C Bricks for Converter
Lining
|
BRAND
|
MC-12b
|
MC-14a
|
MC-14b
|
MC-16a
|
MC-16b
|
|
B.D. (g/cm3) ¡Ý
|
2.98
|
2.98
|
2.98
|
2.95
|
2.90
|
|
A.P. (%) ¡Ü
|
5
|
5
|
5
|
5
|
5
|
|
C.C.S (Mpa) ¡Ý
|
35
|
40
|
35
|
40
|
35
|
|
HOMR (Mpa) ¡Ý
|
7
|
14
|
8
|
12
|
10
|
|
Chemical
Analysis
(%)
|
MgO >
|
76
|
74
|
74
|
72
|
72
|
|
F.C >
|
12
|
14
|
14
|
16
|
16
|
MgO-C Bricks for EAF Lining
|
BRAND |
MC-10b |
MC-14a |
MC-14b |
MC-14c |
MC-14d
|
|
B.D. (g/cm3) ¡Ý
|
3.00 |
2.95 |
2.98 |
2.98 |
3.00 |
|
A.P. (%) ¡Ü
|
5 |
5 |
5 |
5 |
5 |
|
C.C.S (Mpa) ¡Ý
|
35 |
30 |
35 |
40 |
35 |
|
Chemical
Analysis
(%) |
MgO > |
97.5 |
96.5 |
97 |
97.5 |
98.5 |
|
F.C. > |
10 |
14 |
14 |
14 |
14 |
|
SiO2 <
|
0.5 |
0.5 |
0.8 |
0.5 |
0.5 |
|
CaO > |
1.0 |
1.5 |
1.8 |
1.8 |
2.0
|
MgO-C Bricks for Ladles
|
BRAND
|
MC70-10DM |
MC70-15SM |
MC60-10DM |
MC70-15DM |
MC-100
|
MC85-7
|
MC85-10MSI |
MC60-10 |
|
B.D. (g/cm3)
¡Ý
|
2.95
|
2.95
|
2.98
|
2.95
|
2.98
|
2.90
|
2.90
|
2.96
|
|
A.P. (%)
¡Ü
|
3.5
|
4.0
|
4.0
|
3.5
|
3.5
|
3.5
|
3.5
|
3.5
|
|
C.C.S (Mpa)
¡Ý
|
28
|
30
|
30
|
38
|
38
|
32
|
28
|
30
|
|
Chemical Analysis
(%)
|
MgO >
|
97
|
97
|
96
|
97
|
97
|
96
|
96
|
96
|
|
F.C >
|
10
|
15
|
10
|
15
|
18
|
7
|
10
|
10
|
MgO-C Bricks for Ladles
|
BRAND
|
MC70-10DM
|
MC70-15SM
|
MC60-10DM
|
MC70-15DM
|
MC-100
|
MC85-7
|
MC85-10MSI |
MC60-10
|
|
B.D. (g/cm3)
¡Ý
|
2.95
|
2.95
|
2.98
|
2.95
|
2.98
|
2.90
|
2.90
|
2.96
|
|
A.P. (%)
¡Ü
|
3.5
|
4.0
|
4.0
|
3.5
|
3.5
|
3.5
|
3.5
|
3.5
|
|
C.C.S (Mpa)
¡Ý
|
28
|
30
|
30
|
38
|
38
|
32
|
28
|
30
|
|
Chemical
Analysis
(%)
|
MgO >
|
97
|
97
|
96
|
97
|
97
|
96
|
96
|
96
|
|
F.C >
|
10
|
15
|
10
|
15
|
18
|
7
|
10
|
10
|
|